Effect of Ni on phase stability and thermal expansion of Cu 6-xNi xSn 5 (X = 0, 0.5, 1, 1.5 and 2)

K. Nogita, D. Mu, S. D. McDonald, J. Read, Y. Q. Wu

Research output: Contribution to journalArticlepeer-review

65 Citations (Scopus)


The crystallography of the Cu 6Sn 5 intermetallic that forms at the solder-substrate interface in many soldering operations can be influenced by Ni additions. It has been established that when Ni is present at 5-9 at%, the high-temperature hexagonal Cu 6Sn 5 (η) does not transition to the low-temperature monoclinic Cu 6Sn 5 (η′) at the equilibrium temperature of 186°C. In fact, the hexagonal phase remains stable from room temperature to 250°C. This paper shows the stabilising effect of Ni exists in the range of 4.6-17.2 at% Ni in stoichiometric samples, over the larger temperature range of -100 to 250°C using synchrotron X-ray diffraction. The results are also used in combination with dilatometry experiments and show that Ni decreases the magnitude of thermal expansion, and prevents the discontinuity in expansion that occurs with the polymorphic transformation.

Original languageEnglish
Pages (from-to)78-85
Number of pages8
Publication statusPublished - Jul 2012
Externally publishedYes

All Science Journal Classification (ASJC) codes

  • General Chemistry
  • Mechanics of Materials
  • Mechanical Engineering
  • Metals and Alloys
  • Materials Chemistry


Dive into the research topics of 'Effect of Ni on phase stability and thermal expansion of Cu 6-xNi xSn 5 (X = 0, 0.5, 1, 1.5 and 2)'. Together they form a unique fingerprint.

Cite this