Abstract
The effect of 1% Fe and/or 5% Zr (mass%) additions on ω phase formation was investigated for the Ti-15Mo alloy by means of X-ray diffraction analysis and hardness testing. Upon water quenching following solution treatment in the β phase region, the athermal ω phase formation could not be observed in all the alloys, regardless of Fe and Zr additions. The lattice parameter of the β phase decreases with Fe addition, while it increases with Zr addition. Solid solution strengthening by Fe and Zr is not recognized for the β phase. The isothermal ω phase formed after aging at 723 K and 773 K for 3.6 ks, which results in a decrease in the lattice parameter of the β phase and an increase in the hardness. The isothermal ω phase formation is suppressed with Fe and/or Zr additions. This is interpreted as the consequence of the increase in the average value of the bond order (Bo) for the Ti-15Mo-5Zr and Ti-15Mo-5Zr-1Fe alloys, and of the decrease in the average value of the metal d-orbital energy level (Md) for the Ti-15Mo-1Fe alloy. In addition, the degree of the suppression of isothermal ω phase can be predicted by the average values of Bo and Md.
| Original language | English |
|---|---|
| Pages (from-to) | 74-78 |
| Number of pages | 5 |
| Journal | Materials Science & Engineering A: Structural Materials: Properties, Microstructure and Processing |
| Volume | 497 |
| Issue number | 1-2 |
| DOIs | |
| Publication status | Published - Dec 15 2008 |
| Externally published | Yes |
All Science Journal Classification (ASJC) codes
- Materials Science(all)
- Condensed Matter Physics
- Mechanics of Materials
- Mechanical Engineering