Change in electrical resistivity of commercial purity aluminium severely plastic deformed

Yoji Miyajima, Shin Ya Komatsu, Masatoshi Mitsuhara, Satoshi Hata, Hideharu Nakashima, Nobuhiro Tsuji

Research output: Contribution to journalArticlepeer-review

96 Citations (Scopus)


Commercial purity aluminium sheets were severely plastic deformed by accumulative roll bonding (ARB). Changes in electrical resistivity at 77 K and microstructure during the ARB process were traced up to 12 cycles, which corresponded to an equivalent strain of 10. The resistivity at 77 K increased with increasing number of ARB cycles, then saturated after about the sixth ARB cycle with a maximum increment of resistivity from starting material of about 1.1 n m. Since lattice defects affect the resistivity of metals, the internal dislocation density and the density of grain boundaries were evaluated from scanning transmission electron microscopy images using Ham's method and grain boundary maps obtained from electron back-scattering diffraction, respectively. The relationship between the change in resistivity and the lattice defects is discussed.

Original languageEnglish
Pages (from-to)4475-4488
Number of pages14
JournalPhilosophical Magazine
Issue number34
Publication statusPublished - Nov 2010

All Science Journal Classification (ASJC) codes

  • Condensed Matter Physics


Dive into the research topics of 'Change in electrical resistivity of commercial purity aluminium severely plastic deformed'. Together they form a unique fingerprint.

Cite this