Catalytic Synthesis of Nitric Monoxide at the AlN(0001) Surface: Ab Initio Analysis

Pawel Strak, Konrad Sakowski, Pawel Kempisty, Izabella Grzegory, Stanislaw Krukowski

Research output: Contribution to journalArticlepeer-review

4 Citations (Scopus)


Molecular nitrogen and molecular oxygen adsorption at the Al-terminated AlN(0001) surface was investigated using ab initio simulations. It was shown that both species undergo barrierless dissociation during attachment to the surface. The H3 adsorption site was identified as the most favorable for both O and N adatoms. The adsorption energies for O2 and N2 were found to be 14.8 and 6.0 eV, respectively. At the clean surface, separate N and O adatoms have their energies 4.37 eV lower than the NO admolecule. At normal nitrogen pressures, the AlN(0001) surface is fully covered by nitrogen adatoms. It was shown for this coverage that adsorption of oxygen leads to creation of the NO admolecule which is a necessary step for nitric monoxide synthesis. The energetics of NO molecules is related to electronic charge transfer: from the two possible configurations, it is shown that T4 and H3 are donors and acceptors, respectively. The resulting coverage is the mixture of both configurations, controlled by electron charge balance. Thus, the ab initio modeling provides indication that AlN(0001) is the powerful catalyst for high pressure-high temperature synthesis of nitric monoxide (NO), indicating that AlN may be a candidate for applications in industrial mass synthesis of nitrogen-based materials such as fertilizers or explosives.

Original languageEnglish
Pages (from-to)10893-10906
Number of pages14
JournalJournal of Physical Chemistry C
Issue number17
Publication statusPublished - May 2 2019
Externally publishedYes

All Science Journal Classification (ASJC) codes

  • Electronic, Optical and Magnetic Materials
  • General Energy
  • Physical and Theoretical Chemistry
  • Surfaces, Coatings and Films


Dive into the research topics of 'Catalytic Synthesis of Nitric Monoxide at the AlN(0001) Surface: Ab Initio Analysis'. Together they form a unique fingerprint.

Cite this