Affinity of polystyrene films to hydrogen-passivated silicon and its relevance to the Tg of the films

Yoshihisa Fujii, Zhaohui Yang, Jessica Leach, Hironori Atarashi, Keiji Tanaka, Ophelia K.C. Tsui

    Research output: Contribution to journalArticlepeer-review

    142 Citations (Scopus)


    Qualitatively different thickness dependences have been observed in the glass transition temperature, Tg, of polystyrene (PS) films supported by hydrogen-passivated silicon (H-Si). It has been suggested that upon annealing at high temperatures in air, the polymer/substrate interface of these films (i.e., PS/Si), though buried underneath the PS layer, might be oxidized, rendering the films a different polymer/substrate interface (i.e., PS/SiO x-Si), which may account for the different thickness dependences of the Tg observed. In this experiment, we examine if the buried substrate interface of PS/H-Si films can indeed be oxidized by annealing the films at 150 °C in air. Our result shows that a residual film does form on top of the H-Si surface, but it is a bound layer of PS. X-ray photoelectron spectroscopic (XPS) analyses and independence of the residual film on the initial PS thickness evidence that the H-Si substrate buried underneath a PS film is not oxidized by annealing. We discuss a possible explanation to how the different thickness dependences may be observed in the Tg of these films.

    Original languageEnglish
    Pages (from-to)7418-7422
    Number of pages5
    Issue number19
    Publication statusPublished - Oct 13 2009

    All Science Journal Classification (ASJC) codes

    • Organic Chemistry
    • Polymers and Plastics
    • Inorganic Chemistry
    • Materials Chemistry


    Dive into the research topics of 'Affinity of polystyrene films to hydrogen-passivated silicon and its relevance to the Tg of the films'. Together they form a unique fingerprint.

    Cite this