A case study was conducted on the cooling pipe of a pre-cooler which had been used in a 70-MPa hydrogen station demonstration project. The cooling pipe consisted of a main pipe, a mechanical joint pipe and a mechanical joint. The main and mechanical joint pipes had been joined using TIG welding. Through chemical composition analysis, microstructure observation and Vickers hardness measurement, it was revealed that the main and mechanical joint pipes had been manufactured from SUS316L and that 316L was the filler metal used for TIG welding. Round-bar specimens were machined out of the main pipe in order to investigate the tensile properties of the base metal. On the other hand, both round-bar specimen without reinforcement and square-bar specimens with reinforcement were fabricated from the weld-joint. Using the three types of specimens, slow strain rate tensile tests were performed in 0.1 MPa nitrogen gas and in 115 MPa hydrogen gas at a temperature of -40 °C. Reduction of area (RA), φ, for the round base-metal specimen, the round weld-joint specimen and the square weldjoint specimen were respectively, 83.5 %, 71.3 % and 81.4 % in nitrogen gas, whereas the related values in hydrogen gas were 60.1 %, 61.3 % and 40.1 %. In other words, the RA for the three types of specimens was smaller in hydrogen gas than in nitrogen gas. Dimples were formed on the fracture surfaces of the three specimen types in nitrogen gas, whereas both dimples and quasi-cleavages were formed in hydrogen gas.